A repository & source of cutting edge news about emerging terahertz technology, it's commercialization & innovations in THz devices, quality & process control, medical diagnostics, security, astronomy, communications, applications in graphene, metamaterials, CMOS, compressive sensing, 3d printing, and the Internet of Nanothings. NOTHING POSTED IS INVESTMENT ADVICE! REPOSTED COPYRIGHT IS FOR EDUCATIONAL USE.
Tuesday, January 12, 2016
Abstract-Terahertz Saturable Absorption in Superconducting Metamaterials
George R. Keiser, Jingdi Zhang, Xiaoguang Zhao, Xin Zhang, Richard D. Averitt
https://export.arxiv.org/abs/1601.02496
We present a superconducting metamaterial saturable absorber at terahertz frequencies. The absorber consists of an array of split ring resonators (SRRs) etched from a 100nm YBaCu3O7 (YBCO) film. A polyimide spacer layer and gold ground plane are deposited above the SRRs, creating a reflecting perfect absorber. Increasing either the temperature or incident electric field (E) decreases the superconducting condensate density and corresponding kinetic inductance of the SRRs. This alters the impedance matching in the metamaterial, reducing the peak absorption. At low electric fields, the absorption was optimized near 80% at T=10K and decreased to 20% at T=70K. For E=40kV/cm and T=10K, the peak absorption was 70% decreasing to 40% at 200kV/cm, corresponding to a modulation of 43%.
Subscribe to:
Post Comments (Atom)
No comments:
Post a Comment