A repository & source of cutting edge news about emerging terahertz technology, it's commercialization & innovations in THz devices, quality & process control, medical diagnostics, security, astronomy, communications, applications in graphene, metamaterials, CMOS, compressive sensing, 3d printing, and the Internet of Nanothings. NOTHING POSTED IS INVESTMENT ADVICE! REPOSTED COPYRIGHT IS FOR EDUCATIONAL USE.
Thursday, January 1, 2015
Abstract- Microwave and terahertz dielectric properties of MgTiO3–CaTiO3 ceramics
J.B. HuangB. YangC.Y. YuG.F. ZhangH. XueZ.X. XiongG. ViolaR. DonnanH.X. YanM.J. Reece
http://www.sciencedirect.com/science/article/pii/S0167577X14017698?via=ihub
The THz dielectric properties of MgTiO3–CaTiO3 ceramics are reported. The ceramics were prepared via a solid-state reaction route and the sintering conditions were optimized to obtain ceramics with high permittivity and low loss in the terahertz frequency domain. The amount of impurities (MgTi2O5) and grain size increased with increasing sintering temperature. The dielectric properties improved with increasing density, and the best terahertz dielectric performance was obtained at 1260 °C, with a permittivity of 17.73 and loss of 3.07×10−3. Ceramics sintered above 1260 °C showed a sharp increase in loss, which is ascribed to an increase in the impurity content.
Subscribe to:
Post Comments (Atom)
No comments:
Post a Comment