Abstract-Transparent AlON ceramic combined with VO2 thin film for infrared and terahertz smart window

Bo Penga, Qiwu Shia,Wanxia Huanga, Shanshan Wangb, Jianqi Qib,Tiecheng Lub,

https://www.sciencedirect.com/science/article/pii/S0272884218310782


Transparent AlON ceramics are intriguing window materials with excellent mechanical strength and superb optical transparency from the near ultraviolet to the mid-infrared range. However, previous studies focused their investigations in the visible range; therefore, the application of transparent AlON ceramics to tunable windows has yet to be reported. In this work, a VO₂ thin film with a characteristic semiconductor-metal phase transition (SMT) was fabricated on a transparent AlON ceramic, which exhibited remarkable tunable switching properties in the infrared and terahertz ranges. The transparent AlON ceramic was prepared by a two-step method, which included carbothermal reduction and pressureless sintering. The resulting ceramic exhibited high transparency of over 70% in the visible-infrared range and a notable THz transmission of 64.5–73.9% at 0.1–1.5 THz. The VO₂ thin film was prepared on a transparent AlON ceramic using the sol-gel method and showed excellent optical and electric switching performance. The square resistance variance was close to four orders of magnitude, and an infrared switching ratio of over 40% was obtained. Furthermore, the combined structure showed an efficient THz switching ratio of approximately 70.9%. This study proposes a composite material combined with a transparent ceramic and a phase transition oxide and provides great insights into their application in infrared and terahertz smart windows as well as in switching devices.