A repository & source of cutting edge news about emerging terahertz technology, it's commercialization & innovations in THz devices, quality & process control, medical diagnostics, security, astronomy, communications, applications in graphene, metamaterials, CMOS, compressive sensing, 3d printing, and the Internet of Nanothings. NOTHING POSTED IS INVESTMENT ADVICE! REPOSTED COPYRIGHT IS FOR EDUCATIONAL USE.
Pages- Terahertz Imaging & Detection
▼
Monday, October 5, 2015
Abstract-Ultralow temperature terahertz magnetic thermodynamics of perovskite-like SmFeO3 ceramic.
Xiaojian Fu, Xinxi Zeng, Dongyang Wang, Hao Chi Zhang, Jiaguang Han, Tie Jun Cui
http://www.pubfacts.com/detail/26424488/Ultralow-temperature-terahertz-magnetic-thermodynamics-of-perovskite-like-SmFeO3-ceramic
The terahertz magnetic properties of perovskite-like SmFeO3 ceramic are investigated over a broad temperature range, especially at ultralow temperatures, using terahertz time-domain spectroscopy. It is shown that both resonant frequencies of quasi-ferromagnetic and quasi-antiferromagnetic modes have blue shifts with the decreasing temperature due to the enhancement of effective magnetic field. The temperature-dependent magnetic anisotropy constants are further estimated using the resonant frequencies, under the approximation of omitting the contribution of Sm(3+) magnetic moments to the effective field. Specially, the effective anisotropy constants in the ca and cb planes at 3 K are 6.63 × 10(5) erg/g and 8.48 × 10(5) erg/g, respectively. This thoroughly reveals the terahertz magnetic thermodynamics of orthoferrites and will be beneficial to the application in terahertz magnetism.
No comments:
Post a Comment
Please share your thoughts. Leave a comment.